1. The longitudinal tear in the middle of the steel belt is 14-15 meters, how to repair it?
The upper and lower covering glue of the damaged part can be peeled off (the length exceeds the damaged part by 50-100mm, and the width exceeds the damaged part by 30-50mm), and at the same time, take a piece of rubber with the same size as the peeled part (preferably with a layer of cloth), and then It can be repaired according to the cold glue method.
2. Comparison of EP high temperature resistant belt and cotton canvas high temperature resistant belt:
a. The same point: the surface covering glue is the same.
b. Differences: cotton canvas can withstand a maximum temperature of 150 degree ; EP-TNG canvas can be used for a long time at 200 degree , and can be used at a maximum of 220 degree ;
The strength of cotton canvas is relatively low, only 50N/mm; while the strength of EP-TNG canvas is relatively high, and the commonly used type 200 is 200N/mm;
Aderența curelei rezistente la temperaturi înalte din pânză de bumbac este relativ scăzută, iar aderența curelei rezistente la temperaturi înalte EP este relativ ridicată; durata de viață a curelei rezistente la temperaturi înalte EP este evident mai lungă decât cea a curelei rezistente la temperaturi înalte din pânză de bumbac.
3. Hot glue stripping method (is it good to remove the glue at one end)?
Aceasta este o altă metodă de lipire, această metodă este și posibilă, dar dacă utilizați această metodă, acordați atenție următoarelor puncte:
a. Be sure to use sealing glue;
b. The parts where the edge rubber parts meet must be connected by vulcanized rubber;
c. The parts where the rubber is connected must be polished
The disadvantage is that the edge glue part is easily damaged if it is not handled properly.
4. The joint temperature reaches 120 degree , but does not reach the normal vulcanization temperature?
no. The normal vulcanization and crosslinking temperature of rubber is determined by the vulcanizing agent and accelerator in the rubber. In order to ensure the safety of rubber processing, the general manufacturer will not set the vulcanization starting temperature of the rubber used in the conveyor belt to be very low. Therefore, when the temperature reaches 120 degree , the rubber will not enter the normal vulcanization state. Therefore, at 120 degree , the quality of the conveyor belt joint will be greatly affected.
De obicei, atunci când temperatura de vulcanizare este mai mare decât temperatura critică de vulcanizare a acceleratorului și agentului de vulcanizare și nu poate atinge temperatura normală de vulcanizare, metoda de prelungire a timpului de vulcanizare poate fi adoptată pentru a face ca vulcanizarea cauciucului să îndeplinească cerințele. În general, de fiecare dată când temperatura este mai mică de 10 grade, timpul de vulcanizare este prelungit de 2-4 ori. Desigur, din motive de performanță, nu recomandăm utilizarea vulcanizării la temperatură scăzută-și pe termen lung.
5. Can core rubbers from different manufacturers be mixed?
Nu este recomandat să amestecați miez de cauciuc de la diferiți producători, deoarece formula de miez de cauciuc de la diferiți producători este diferită. Există multe tipuri de agenți de amestecare în cauciuc, iar unii dintre ei au reacții interactive. În formula aceluiași producător, nu vor exista agenți de amestecare cu reacții interactive adverse, dar formulele diferiților producători sunt foarte diferite. Când este utilizat, pot exista reflexii interactive ale agenților de amestecare, care vor afecta efectul de utilizare al cauciucului de bază.